In this study, we developed a technology that can measure key evaluation items in the field for various rehabilitation
methods and evaluated its performance. The results are as follows. First, when the spray-on lining adhesion strength
is measured after drying at high temperature (60℃) for 4 hours and cooling for 2 hours, the results are equivalent
to or higher than the adhesion strength measured at room temperature after 48 hours. Therefore, the time required
for measuring the adhesion strength in the field can be shortened to 1/8, and it is expected to be helpful in evaluating
the condition of the spray-on lining. Second, depending on close or adhesive to existing pipe of the liner of the close-fit
lining or CIPP lining, and the grouting condition of the slip lining, the sound frequency generation pattern, the vibration
magnitude, and duration using the impact echo showed different characteristics. Therefore, it is thought that it is possible
to evaluate liner lifting or grouting failure through analysis of the acoustic frequency, vibration magnitude, and duration.
Third, when water penetrates the back of the liner of the close-fit lining or CIPP lining, it was found that the water
penetrated between the liner and the existing pipe acts as a couplant, and a signal is repeatedly generated in which
ultrasonic energy is transmitted and reflected to the steel pipe after the liner. Therefore, it is judged that it is possible
to check whether water has penetrated the back of the liner using ultrasonic waves. Fourth, the liner tensile strength
of the close-fit, CIPP lining was compared with the tensile test and the instrumented indentation test, and it was found
that the tensile strength was similar. So it was judged that it will be helpful in evaluating the mechanical strength change
without the liner specimen in the future.